Strontium and iron-doped barium cobaltite prepared by solution combustion synthesis: exploring a mixed-fuel approach for tailored intermediate temper…
2013
Ba0.5Sr0.5Co0.8Fe0.2O3-? (BSCF) powders were prepared by solution combustion synthesis using single and double fuels. The effect of the fuel mixture on the main properties of this well-known solid oxide fuel cell cathode material with high oxygen ion and electronic conduction was investigated in detail. Results showed that the fuel mixture significantly affected the area-specific resistance of the BSCF cathode materials, by controlling the oxygen deficiency and stabilizing the Co2+ oxidation state. It was demonstrated that high fuel-to-metal cations molar ratios and high reducing power of the combustion fuel mixture are mainly responsible for the decreasing of the area-specific resistance o…
Nanoscale membrane electrode assemblies based on porous anodic alumina for hydrogen–oxygen fuel cell
2007
In this paper, we demonstrate that nanoscale membrane electrode assemblies, functioning in a H 2/O 2 fuel cell, can be fabricated by impregnation of anodic alumina porous membranes with Nafion® and phosphotungstic acid. Porous anodic alumina is potentially a promising material for thin-film micro power sources because of its ability to be manipulated in micro-machining operations. Alumina membranes (Whatman, 50 μm thick, and pore diameters of 200 nm) impregnated with the proton conductor were characterized by means of scanning electron microscopy, X-ray diffraction, and thermal analysis. The electrochemical characterization of the membrane electrode assemblies was carried out by recording t…
On the merit of a Central Limit Theorem-based approximation in statistical physics
2012
The applicability conditions of a recently reported Central Limit Theorem-based approximation method in statistical physics are investigated and rigorously determined. The failure of this method at low and intermediate temperature is proved as well as its inadequacy to disclose quantum criticalities at fixed temperatures. Its high temperature predictions are in addition shown to coincide with those stemming from straightforward appropriate expansions up to (k_B T)^(-2). Our results are clearly illustrated by comparing the exact and approximate temperature dependence of the free energy of some exemplary physical systems.
Surface Segregation Entropy of Protons and Oxygen Vacancies in BaZrO3
2016
The perovskite BaZrO3 has attracted considerable attention in the recent decade due to its high temperature proton conducting properties, and possible application as electrolyte in intermediate temperature fuel cells and electrolyzers. In this contribution, we performed, for the first time, first-principles calculations of the phonon contribution to the defect thermodynamics of the ZrO2 terminated (001) surface of BaZrO3. The approach allows us to determine both the segregation enthalpy and entropy of defects, which we apply to two fundamental defects in BaZrO3; fully charged oxygen vacancies (vO••) and protonic defects (OHO•). The calculations show that both defects exhibit favorable segre…
Nanoporous alumina membranes filled with solid acid for thin film fuel cells at intermediate temperatures
2004
Thin film fuel cells have been fabricated by impregnation of inorganic porous membranes with inorganic proton conductor. Anodic alumina membranes (50 μm thick and pore diameter of 200 nm), filled with CsHSO4 salt have been used as protonic conductor in a hydrogen-oxygen fuel cell working between 423 and 443 K in dry atmosphere. Polarization curves at 433 K showing ohmic control with open circuit values near 0.8 V and short circuit current around 8 mA cm−2 have been obtained. Possible causes of degradation as well as alternative routes to overcome some of the problems encountered with this approach will be reported. Keywords: Solid acid, Anodic alumina membranes, Pore filling, Thin film fuel…